Comparative analysis of ceramic-carbonate nanocomposite fuel cells using composite GDC/NLC electrolyte with different perovskite structured cathode materials

Loading...
Thumbnail Image
Journal Title
Journal ISSN
Volume Title
A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä
Date
2018
Major/Subject
Mcode
Degree programme
Language
en
Pages
12
162–173
Series
FRONTIERS OF CHEMICAL SCIENCE AND ENGINEERING, Volume 12, issue 1
Abstract
A comparative analysis of perovskite structured cathode materials, La0.65Sr0.35MnO3 (LSM), La0.8Sr0.2CoO3 (LSC), La0.6Sr0.4FeO3 (LSF) and La0.6Sr0.4Co0.2Fe0.8O3 (LSCF), was performed for a ceramic-carbonate nanocomposite fuel cell using composite electrolyte consisting of Gd0.1Ce0.9O1.95 (GDC) and a eutectic mixture of Na2CO3 and Li2CO3. The compatibility of these nanocomposite electrode powder materials was investigated under air, CO2 and air/CO2 atmospheres at 550 °C. Microscopy measurements together with energy dispersive X-ray spectroscopy (EDS) elementary analysis revealed few spots with higher counts of manganese relative to lanthanum and strontium under pure CO2 atmosphere. Furthermore, electrochemical impedance (EIS) analysis showed that LSC had the lowest resistance to oxygen reduction reaction (ORR) (14.12 Ω∙cm2) followed by LSF (15.23 Ω∙cm2), LSCF (19.38 Ω∙cm2) and LSM (>300 Ω∙cm2). In addition, low frequency EIS measurements (down to 50 μHz) revealed two additional semi-circles at frequencies around 1 Hz. These semicircles can yield additional information about electrochemical reactions in the device. Finally, a fuel cell was fabricated using GDC/NLC nanocomposite electrolyte and its composite with NiO and LSCF as anode and cathode, respectively. The cell produced an excellent power density of 1.06 W/cm2 at 550 °C under fuel cell conditions. [Figure not available: see fulltext.]
Description
Keywords
electrode, fuel cell, low-temperature, nanocomposite, perovskite
Other note
Citation
Asghar , I , Lepikko , S , Patakangas , J , Halme , J & Lund , P D 2018 , ' Comparative analysis of ceramic-carbonate nanocomposite fuel cells using composite GDC/NLC electrolyte with different perovskite structured cathode materials ' , FRONTIERS OF CHEMICAL SCIENCE AND ENGINEERING , vol. 12 , no. 1 , pp. 162–173 . https://doi.org/10.1007/s11705-017-1642-2